1. The longitudinal tear in the middle of the steel belt is 14-15 meters, how to repair it?
The upper and lower covering glue of the damaged part can be peeled off (the length exceeds the damaged part by 50-100mm, and the width exceeds the damaged part by 30-50mm), and at the same time, take a piece of rubber with the same size as the peeled part (preferably with a layer of cloth), and then It can be repaired according to the cold glue method.
2. Comparison of EP high temperature resistant belt and cotton canvas high temperature resistant belt:
a. The same point: the surface covering glue is the same.
b. Differences: cotton canvas can withstand a maximum temperature of 150 degree ; EP-TNG canvas can be used for a long time at 200 degree , and can be used at a maximum of 220 degree ;
The strength of cotton canvas is relatively low, only 50N/mm; while the strength of EP-TNG canvas is relatively high, and the commonly used type 200 is 200N/mm;
Puuvillasest lõuendist kõrge temperatuurikindla vöö nakkuvus on suhteliselt madal ja EP kõrge temperatuurikindla vöö nakkuvus on suhteliselt kõrge; EP kõrge temperatuurikindla rihma kasutusiga on ilmselgelt pikem kui puuvillasest lõuendist kõrge temperatuurikindla rihma kasutusiga.
3. Hot glue stripping method (is it good to remove the glue at one end)?
See on veel üks liimimismeetod, see meetod on samuti võimalik, kuid kui kasutate seda meetodit, pöörake tähelepanu järgmistele punktidele:
a. Be sure to use sealing glue;
b. The parts where the edge rubber parts meet must be connected by vulcanized rubber;
c. The parts where the rubber is connected must be polished
The disadvantage is that the edge glue part is easily damaged if it is not handled properly.
4. The joint temperature reaches 120 degree , but does not reach the normal vulcanization temperature?
no. The normal vulcanization and crosslinking temperature of rubber is determined by the vulcanizing agent and accelerator in the rubber. In order to ensure the safety of rubber processing, the general manufacturer will not set the vulcanization starting temperature of the rubber used in the conveyor belt to be very low. Therefore, when the temperature reaches 120 degree , the rubber will not enter the normal vulcanization state. Therefore, at 120 degree , the quality of the conveyor belt joint will be greatly affected.
Tavaliselt, kui vulkaniseerimistemperatuur on kõrgem kui kiirendi ja vulkaniseerimisaine kriitiline vulkaniseerimistemperatuur ega saavuta normaalset vulkaniseerimistemperatuuri, võib kummi vulkaniseerimise nõuetele vastavaks muutmiseks kasutada vulkaniseerimisaja pikendamise meetodit. Üldiselt pikeneb vulkaniseerimisaeg iga kord, kui temperatuur on alla 10 kraadi, 2-4 korda. Loomulikult ei soovita me jõudluse huvides kasutada madalat-temperatuuri ja pikaajalist vulkaniseerimist.
5. Can core rubbers from different manufacturers be mixed?
Erinevate tootjate südamikukummi ei ole soovitatav segada, kuna erinevate tootjate südamikukummi valem on erinev. Kummis on palju erinevaid koostisaineid ja mõnel neist on interaktiivsed reaktsioonid. Sama tootja valemis ei ole kõrvaltoimeid tekitavaid koostisaineid, kuid erinevate tootjate valemid on väga erinevad. Kasutamisel võivad esineda seguainete interaktiivsed peegeldused, mis mõjutavad kummi südamiku kasutusefekti.